Easy Mix RK 7000 Structural Acrylic Adhesive 50ml

Composition

 Methyl methacrylate

Colour after curing

cream white, milky

Mixing ratio resin/hardener

1:1

Density of the mixture

0,98 - 1,02 g/cm³

Viscosity of the mixture

40.000 - 60.000 mPa·s

Application

procedure Easy-Mix

Composition

viscous

Pot-life at +20°C (+68°F)

15 min.

Handling strength (35% strength) after

40 min.

Capable of bearing mechanical loads (50% strength) after

 60 min.

Processing temperature

+10 to +40 °C

Curing temperature

+18 °C

Final strength (100%) after

12 h

Tensile strength ISO 527 max.

24 N/mm2

Strength-E-Module (DIN EN ISO 527)

1200 - 1500 Mpa

Elongation at break (DIN EN ISO 527)

28 %

Adhesive gap bridging

0,1 - 5,0 mm

Aluminium

20 N/mm2

Steel sand blasted

23 N/mm2

Stainless Steel

22 N/mm2

PC

11 N/mm2

Tg after curing at room temperature

-39,8 Tg (deg C)

PMMA

9 N/mm2

ABS

7 N/mm2

Hard-PVC

12 N/mm2

GRP

21 N/mm2

CFK

22 N/mm2

Polyamide

6.6 1 N/mm2

Temperature resistance

-55 to +125 deg C

Thermal diffusivity (23 deg C)

 0,118 mm2/s

Thermal conductivity

0,20 W/m·K

Specific heat capacity

1,453 J/(g·K)

ISSA-Code

75.629.55

IMPA-Code

812994