Fast Metal Minute Adhesive 24Ml

Base

Epoxy resin highly filled

Composition

Pasty consistency, crack-filler

Colour

Grey

Mixing ratio by weight (Resin / Hardener)

 1:1

Density of the mixture

1,8 g/cm3

Adhesive gap bridging up to max.

 4 mm

Processing temperature

+10 to +30 deg C

Curing temperature

+6 to +40 deg C

Pot-life at 20 deg C (+68 deg F) for 10ml material

 3 -4 min.

Handling strength (35% strength) after

 40 min.

Capable of bearing mechanical loads (50% strength) after

2 h

Final strength (100%) after

24 h

Pressure

10 Mpa

Pull

24 Mpa

Bending

58 Mpa

Shore hardness D

70

Steel sand blasted

20 N/mm2

Alu sandblasted

19 N/mm2

PVC hard-roughened

11 N/mm2

Linear shrinkage

 0,3 %

Temperature resistance

-50 to +145 deg C

ISSA-Code

75.629.51

IMPA-Code

81 29 81