Stainless Steel Aerosol Spray Bright Grade 400 Ml

Colour

stainless steel metallic

Application

indoors and outdoors

Binding agent

acrylic resin

Pigment

stainless steel and aluminium pigments

Pigment purity

VA-alloy approx. 98,5 % Al

Percentage of metal in dry film

35 %

Specific weight

0,9 - 1,0 g/cm3

Recommended primer

Zinc-Spray

Processing temperature

+5 to +35, optimal +18 to +35 deg C

Consumption at 1.5 cross coats

120 ml/m2

Layer thickness at 1.5 cross coats

15-25  m

Dust dry after

10 min.

Hardened after

10 h

Overpaintable after

8 h

Abrasion-resistant yes/no

abrasion-resistant

Cross cutting DIN 53151/ ISO 2409

cross cut characteristic value GT 0 to GT 1

Salt spraying test DIN EN ISO 9227

>140 h

Mandrel bend test DIN EN ISO 1519

no hair cracking

Top coating

not required

Storage stability

24 months

Temperature resistance

-50 to +300 deg C