Zinc Metal Spray

Processing temperature

 +5 to +35, optimal +18 to +35 deg C

Consumption at 1.5 cross coats

150 ml/m2

Layer thickness at 1.5 cross coats

30 -50 m

Dust dry after

15 min.

Hardened after

12 h

Overpaintable after

24 h

Abrasion-resistant yes/no

abrasion-resistant

Cross cutting DIN 53151/ ISO 2409

cross cut characteristic value GT 0

Salt spraying test DIN EN ISO 9227

>1.050 h

Mandrel bend test DIN EN ISO 1519

no hair cracking

Top coating

not required

Storage stability

24 months

Temperature resistance

-50 to +500 deg C

ISSA-Code

53.402.06

IMPA-Code

45 08 11

Colour

RAL 9006,  Slightly weathered hot-dip galvanisation

Application

indoors and outdoors

Binding agent

styrenated alkyd resin

Pigment

flaky zinc and aluminium pigments

Pigment purity

approx. 99,9% Zn / approx. 99,9% Al

Percentage of metal in dry film

70 %

Specific weight

1,1 - 1,3 g/cm3

Recommended primer

not required