Epoxy Repair Stick Aluminium 115 G

Composition

Epoxy resin aluminium-filled

Composition

Pasty

Colour after curing

Aluminium

Mixing ratio by volume resin/hardener

1:1

Density of the mixture

1,9 g/cm3

Gap bridging max.

15 mm

Processing temperature

+10 to +35 deg C

Curing temperature

+6 to +40 deg C

Polt life for 25gr preparation and +20 deg C (+68 deg F)

4 min.

Handling strength (35%) after

10 min.

Mechanical loads (50% strength) after

60 min.

Final strength (100%) after

24 h

Pressure (DIN 53281-83)

80 N/mm2

Medium shear strength after 7 days at +20 deg C (+65 deg F) DIN 532832 at

Aluminium sandblasted: 4,2 N/mm2

Shore hardness D

75

Thermal conductivity (ASTM D 257)

0,65 W/m.K

Linear shrinkage

<1 %

Dielectric strength (ASTM D 149)

3,0 kV/mm

Temperature resistance

-50 to +120 briefly +150 deg C

ISSA-Code

75.530.10/11

IMPA-Code

81 29 65/66