Plastic Bond Compound 24ml

Base

Methyl methacrylate

Colour after curing

 cream white, milky

Mixing ratio resin/hardener

 1:1

Density of the mixture

0,98 - 1,02 g/cm³

Viscosity of the mixture

40.000 - 60.000 mPa·s

Application

procedure A-B-method

Composition

 thixotropic

Pot-life at +20°C (+68°F)

15 min.

Handling strength (35% strength) after

 40 min.

Capable of bearing mechanical loads (50% strength) after

60 min

Processing temperature

+10 to +40 °C

Curing temperature

 +18 °C

Final strength (100%) after

 12 h

Adhesive gap bridging

0,1 - 5,0 mm

Aluminium

20 N/mm²

Steel sand blasted

23 N/mm²

Stainless Steel

22 N/mm²

PC

 11 N/mm²

PMMA

9 N/mm²

ABS

 7 N/mm²

Hard-PVC

12 N/mm²

GRP

21 N/mm²

CRP

22 N/mm²

Polyamide

6.6 1 N/mm²

Temperature resistance

-55 to +125 °C