WEICON CBC Epoxy Resin 3.0 kg

Base

Epoxy resin aluminium-filled

Specific Properties

liquid, impact resistant

Colour after curing

 grey

Mixing ratio by weight resin/hardener

100 by 30

Density of the mixture (200g preparation)

1,5 g/cm3

Consumption at a coating thickness of 1,0 mm

1,50 kg/m2

Curing time mechanical loads

12 h

Final hardness after

24 h

Mean compressive strength (DIN EN ISO 604)

70 Mpa

Strength-E-Module (DIN EN ISO 527)

4.170 Mpa

Elongation at break (DIN EN ISO 527)

0,7 %

Impact strength (ISO 179-1/1eU)

3,7 kJ/m2

Shore D (ATSM D 1706)

80

Shrinkage

 0,1 %

Tg after curing at room temperature

51,5 deg C

Tg after tempering (at 120 deg C)

77,1 deg C

Temperature resistance

-40 to +160 deg C

Thermal diffusivity (23 deg C)

 0,312 mm2/s