WEICON Ceramic BL Epoxy Resin 0.5 kg

Composition

 Epoxy resin mineral-filled

Specific Properties

liquid, extremely wear resistant

Colour after curing

Blue

Density of the mixture (200g preparation)

1,8 g/cm3

Consumption at a coating thickness of 1,0 mm

1,80 kg/m2

Maximium layer thickness for each working step

10 mm

Pot life at +20 deg C (+68 deg F) 200g preparation

55 min.

Curing time mechanical loads

16 h

Final hardness after

24 h

Pressure

120 Mpa

Pull

22 Mpa

Bending

80 Mpa

Shore D (ATSM D 1706)

93

Shrinkage

 0,02 %

Thermoforming resistance

+95 deg C

Temperature resistance

-35 to +180 deg C

ISSA-Code

75.509.19/20

IMPA-Code

812937/38