WEICON HB 300 Epoxy Resin 1.0 kg

Composition

Epoxy resin steel-filled

Specific Properties

Putty , high-temp. resistant

Colour after curing

Dark -grey

Density of the mixture (200g preparation)

2,34 g/cm3

Consumption at a coating thickness of 1,0 mm

2,34 kg/m2

Maximum layer thickness for each working step

20 mm

Pot life at +20 deg C (+68 deg F) 200g preparation

30 min.

Curing time mechanical loads

12 h

Final hardness after

24 h

Pressure

100 Mpa

Pull

27 Mpa

Bending

42 Mpa

Shore D (ATSM D 1706)

85

Shrinkage

0,015 %

Tg after curing at room temperature

 57,1 Tg (deg C)

Tg after tempering (at 120 deg C)

92,4 Tg (deg C)

Thermoforming resistance

+120 deg C

Temperature resistance

-35 to +200 briefly to +280 deg C

Thermal diffusivity (23 deg C)

0,345 mm2/s

ISSA-Code

75.509.21

IMPA-Code

 812951