WEICON WR Epoxy Resin 2.0 kg

Base

Epoxy resin steel-filled

Specific Properties

 liquid, wear resistant

Colour after curing

black

Density of the mixture (200g preparation)

2,3 g/cm3

Consumption at a coating thickness of 1,0 mm

2,30 kg/m2

Maximium layer thickness for each working step

10 mm

Pot life at +20 deg C (+68 deg F) 200g preparation

45 min.

Curing time mechanical loads

16 h

Final hardness after

24 h

Pressure

110 Mpa

Pull

33 Mpa

Bending

80 Mpa

Shore D (ATSM D 1706)

90

Shrinkage

0,02 %

Tg after curing at room temperature

53,8 Tg (deg C)

Tg after tempering (at 120  deg C)

70,1 Tg (deg C)

Thermoforming resistance

+65 deg C

Temperature resistance

-35 to +120 deg C

Thermal diffusivity (23deg C)

0,717 mm2/s

ISSA-Code

75.509.15/16

IMPA-Code

812947/48