WEICON BR Epoxy Resin 0.5 kg

Composition

Epoxy resin bronze-filled

Specific Properties

Pasty

Colour after curing

Bronze

Density of the mixture (200g preparation)

1,8 g/cm3

Consumption at a coating thickness of 1,0 mm

1,80 kg/m2

Maximum layer thickness for each working step

12 mm

Pot life at +20 deg C (+68 deg F) 200g preparation

60 min.

Curing time mechanical loads

16 h

Final hardness after

24 h

Pressure

95 Mpa

Pull

29 Mpa

Bending

35 Mpa

Shore D (ATSM D 1706)

75

Shrinkage

0,02 %

Tg after curing at room temperature

47,2 Tg (deg C)

Tg after tempering (at 120 deg C)

46,2 Tg (deg C)

Thermoforming resistance

+50 deg C

Temperature resistance

-35 to +120 deg C

Steel sand blasted

18 MPa

Sandblasted stainless steel

20 MPa

Sand-blasted Aluminium

12 MPa

Galvanized steel

7 MPa

Thermal diffusivity (23 deg C)

0,365 mm2/s

ISSA-Code

75.509.05/06

IMPA-Code

812910/11