WEICON A Epoxy Resin 0.5 kg

Composition

Epoxy resin steel filled

Specific Properties

pasty

Colour after curing

dark grey

Mixing ratio by weight resin/hardener

100 10

Density of the mixture (200g preparation)

2,9 g/cm3

Viscosity of the mixture

1.000.000 mPa.s

Consumption at a coating thickness of 1,0 mm

2,9 kg/m2

Maximum layer thickness for each working step

10 mm

Curing time mechanical loads

16 h

Final hardness after

24 h

Pressure

80 Mpa

Pull

21 Mpa

Bending

34 Mpa

E-Modul

3.500 - 5.000 Mpa

Shore D (ATSM D 1706)

90

Shrinkage

0.015 %

Tg after curing at room temperature

60,9 Tg (deg C)

Tg after tempering (at 120 deg C)

 78 Tg (deg C)

Thermoforming resistance

+65 deg C

Temperature resistance

-35 to +120 deg C

Steel sand blasted

11,6 MPa