WEICON WR2 Epoxy Resin 2.0 kg

Base

 Epoxy resin mineral-filled

Specific Properties

putty, wear resistant

Colour after curing

dark-grey

Density of the mixture (200g preparation)

 1,67 g/cm3

Consumption at a coating thickness of 1,0 mm

1,67 kg/m2

Maximum layer thickness for each working step

10 mm

Pot life at +20 deg C (+68 deg F) 200g preparation

45 min.

Curing time mechanical loads

16 h

Final hardness after

24 h

Pressure

71 Mpa

Pull

29 Mpa

Bending

39 Mpa

Shore D (ATSM D 1706)

82

Shrinkage

 0,025 %

Tg after curing at room temperature

53,5 Tg (deg C)

Tg after tempering (at 120 deg C)

58,9 Tg (deg C)

Thermoforming resistance

+65 deg C

Temperature resistance

-35 to +120 deg C